河北科技大学学报2017，Vol.38Issue(6)：585-589,5.DOI:10.7535/hbkd.2017yx06012
磁性法分析束状贝氏体基体渗碳钢
Analysis of carburizing steel with lath bainite in matrix by magnetic method
摘要
Abstract
The cryogenic treatment is used to reduce the large amount of retained austenite in the steel infiltration layer which affects the hardness.The vibrating sample magnetometer (VSM)and direct reading spectroscopy are combined to compare and analyze the organization structure status of the test carburizing steel after air-cooling and low temperature tempering (T)at 453 K × 1 h,or after cryogenic treatment at 113 K × 30 min and low temperature tempering (T)at 453 K × 1 h.The cryopreservation effect of the 1203 K × 9 h carburizing air-cooled bainitic steel is carried out.The results show that both the effective hardening layer depths are about 1.35 mm.The retained austenite mass fractions of T and CT in the effective hardened layer are approximately 29.8% and 12.6%,respectively,and the highest hardnesses of the effective hardened layer of T and CT are 679 HV and 821 HV,respectively.The matrix structure is lath bainite,and the retained austenite mass fractions in the matrix are approximately 7.4% for T and 6.9% for CT,respectively,and both the hardnesses of the matrixes are approximately 430 HV.After the cryogenic treatment,the austenite content in the infiltration layer is effectively reduced,so that the maxi-mum hardness of the hardened layer increases by 20% or more.It can be widely used because of the decreased material cost and remarkable economical benefit.关键词
热处理工艺与设备/组织/有效硬化层/深冷处理/振动样品磁强计/残留奥氏体/回火Key words
heat treatment process and equipment/microstructure/effective hardened layer/cryogenic treatment(C)/vibrating sample magnetometer(VSM)/retained austenite/tempering(T)分类
矿业与冶金引用本文复制引用
邹卫武,孙世清,刘家鹏,程世超,王仕东..磁性法分析束状贝氏体基体渗碳钢[J].河北科技大学学报,2017,38(6):585-589,5.基金项目
国家自然科学基金(51774108) （51774108）