铁道科学与工程学报2018，Vol.15Issue(1)：94-102,9.
预拌-增强型复合结合料性能评价
The performance of pre-mixed and enhanced binder
仰建岗 1刘同宾 2李杨 1王志祥 3张争奇4
作者信息
- 1. 江西省高速公路养护工程技术研究中心,江西 南昌 330103
- 2. 华东交通大学 土木建筑学院,江西 南昌 330013
- 3. 江西省天驰高速科技发展有限公司,江西 南昌 330103
- 4. 长安大学 公路学院,陕西 西安 710064
- 折叠
摘要
Abstract
"The pre-mixed & enhanced" mixing process that means the mixture can be constructed under relatively lower temperature and show good performances at high and low temperature, resulting the best economic and environmental benefits. In this study, firstly, the natural asphalt performance improvement mechanism was studied through SEM and Fluorescence Microscope based on the micro modification mechanism. And then, Orthogonal Experiment was carried out to determine the preparation technology. Last, the performance of asphalt compound binding material with different types and percent were analyzed,the research shows that there is a stable structure of micro heterogeneous and macro evenly between natural and soft asphalt. Futhermore, the research indicated that the high temperature property and aging performance of binder are improved, while low temperature performance is reduced. To sum up, the great doses are 25% percent for TLA and Buton asphalt, besides, 8% for Qing Chuan and Albania asphalt.关键词
预拌-增强/天然沥青/软质沥青/改性机理/制备工艺Key words
ready mixed-enhanced/natural asphalt/soft asphalt/modification mechanism/preparation technology分类
交通工程引用本文复制引用
仰建岗,刘同宾,李杨,王志祥,张争奇..预拌-增强型复合结合料性能评价[J].铁道科学与工程学报,2018,15(1):94-102,9.