电池2017，Vol.47Issue(6)：351-353,3.DOI:10.19535/j.1001-1579.2017.06.009
Al包覆三元前驱体Ni0.6Co0.2Mn0.2(OH)2的性能
Performance of Al coated ternary precursor Ni0.6Co0.2Mn0.2 (CH)2
李伟权 1刘更好1
作者信息
- 1. 广东邦普循环科技有限公司,广东佛山528244
- 折叠
摘要
Abstract
Using Al2 (SO4) 3 as aluminum source,ammonia as precipitant and ammonium oxalate as chelating agent,a coating layer was formed on the surface of Ni0.6 Co0.2 Mn0.2 (OH) 2 particles by wet-way precipitation method,according to the theory of heterogeneous nucleation.The agglomeration of Al(OH) 3 and the adhesion between coated particles were improved,the influence of coating on the tap density and particle sizes of the material was reduced.The uniform and dense coating layer was formed when the mole ratio of ammonium oxalate and Al2 (SO4)3 was 3∶ 1.The shell like structure was formed when the content of Al was 1％.The network structure and the dot coating structure were formed when the content of Al were 0.5％ and 0.3％.关键词
络合剂/Ni0.6Co0.2Mn0.2(OH)2前驱体/铝包覆/非均匀成核/团聚/锂离子电池Key words
chelating agent/Ni0.6 Co0.2 Mn0.2 (OH) 2 precursor/Al coating/heterogeneous nucleation/agglomeration/Li-ion battery分类
信息技术与安全科学引用本文复制引用
李伟权,刘更好..Al包覆三元前驱体Ni0.6Co0.2Mn0.2(OH)2的性能[J].电池,2017,47(6):351-353,3.