预合金粉结合剂真空无压烧结制备金刚石工具OA北大核心CSTPCD
Preparing diamond tool at vacuum pressureless sintering with pre-alloy powder binder
以Fe40Cu40Co20和Cu80Sn20预合金粉为结合剂,采用真空无压烧结制备金属胎体样品,并与相同烧结工艺下的金属单质粉结合剂烧结样品进行对比.用扫描电子显微镜、洛氏硬度计、阿基米德排水法对所得样品的微观形貌、硬度和相对致密度进行对比分析.研究发现:随温度升高,两类样品的致密度和硬度均先增大后减小;当烧结温度达到860℃时,致密度和硬度均达到最大值.预合金粉在860℃下烧结所得样品的相对致密度比同条件下烧结的金属单质粉样品的提高5％,硬度提…查看全部>>
Diamond tool binder samples were prepared using vacuum and pressureless sintering with Fe40Cu40Co20 and Cu80Sn20 pre-alloy powder as raw material.The samples were compared with those sintered at the same process and elements but with mixed metal powder.The hardness,density and matrix morphology of matrices with pre-alloy powder and mixed metal powder were compared and analyzed using Rockwell hardness tester,Archimedes Drainage Act and SEM,respectively.Result…查看全部>>
侯明;郭胜惠;高冀芸;杨黎;彭金辉;王梁;叶小磊;梁宝岩
国家超硬材料先进制备技术国际联合研究中心,昆明650093昆明理工大学冶金与能源工程学院,昆明650093国家超硬材料先进制备技术国际联合研究中心,昆明650093复杂有色金属资源清洁利用国家重点实验室,昆明650093微波能工程应用和装备技术国家地方联合工程实验室,昆明650093昆明理工大学冶金与能源工程学院,昆明650093云南民族大学化学与环境学院,昆明650500国家超硬材料先进制备技术国际联合研究中心,昆明650093
化学化工
预合金粉真空无压烧结硬度致密度
pre-alloyed powdervacuum pressureless sinteringhardnessdensity