江苏大学学报（自然科学版）2018，Vol.39Issue(2)：217-221,5.DOI:10.3969/j.issn.1671-7775.2018.02.016
激光冲击强化对42CrMo钢耐高温腐蚀性能的影响
Influence of laser shock processing on high temperature corrosion behavior of 42CrMo alloy steel
摘要
Abstract
The laser shock processing(LSP)was carried out for 42CrMo alloy steel with high energy nanosecond pulse laser.Residual stress,hardness and roughness of 42CrMo alloy steel were determined after LSP.The high temperature corrosion tests of untreated and treated samples by LSP were conducted. The surface micro-topography of 42CrMo alloy steel was observed by scanning electron microscope(SEM) to investigate the high temperature corrosion resistance of 42CrMo alloy steel.The results show that the corrosion morphology of the specimen after LSP is obviously better than that without LSP.The enhancement of high temperature corrosion resistance of 42CrMo steel after LSP is mainly due to the existence of residual compressive stress layer on material surface,which can inhibit the oxide film from falling off and improve the high temperature corrosion resistance.Compared with small energy laser shock,the large energy impact can greatly increase the compressive residual stress of specimen surface and enhance the influence of residually compressive stress.关键词
42CrMo合金钢/激光冲击/高温腐蚀/残余压应力/硬度Key words
42CrMo alloy steel/laser shock/high temperature corrosion/residual stress/hardness分类
信息技术与安全科学引用本文复制引用
李传君,李凯,黄婉婉,陆益顺,吕东明,王志强,俞婷,韩彬..激光冲击强化对42CrMo钢耐高温腐蚀性能的影响[J].江苏大学学报（自然科学版）,2018,39(2):217-221,5.基金项目
"十二五"国家重大科技专项(2011ZX05024-005 -004) （2011ZX05024-005 -004）