首页|期刊导航|中国铸造|Solidification pathways and hot tearing susceptibility of MgZnxY4Zr0.5 alloys

Solidification pathways and hot tearing susceptibility of MgZnxY4Zr0.5 alloys

Zhi Wang Sheng Yao Yu Feng Zheng Liu Yi-zhou Li Feng Wang Ping-li Mao

中国铸造2018，Vol.15Issue(2)：124-131,8.

Solidification pathways and hot tearing susceptibility of MgZnxY4Zr0.5 alloys

Zhi Wang ¹Sheng Yao ¹Yu Feng ¹Zheng Liu ¹Yi-zhou Li ¹Feng Wang ¹Ping-li Mao¹

作者信息

1. School of Materials Science and Engineering, Shenyang University of Technology, Shenyang 110870, China
折叠

摘要

关键词

MgZnxY4Zr0.5alloys/microstructure/thermal analysis/hot tearing susceptibility

Key words

MgZnxY4Zr0.5alloys/microstructure/thermal analysis/hot tearing susceptibility

分类

矿业与冶金

引用本文复制引用

Zhi Wang,Sheng Yao,Yu Feng,Zheng Liu,Yi-zhou Li,Feng Wang,Ping-li Mao..Solidification pathways and hot tearing susceptibility of MgZnxY4Zr0.5 alloys[J].中国铸造,2018,15(2):124-131,8.

基金项目

This work was financially supported by the National Natural Sciences Foundation of China (No.51504153, No.51571145), and the General Project of Scientific Research of the Education Department of Liaoning Province (No.L2015397). （No.51504153, No.51571145）

中国铸造

OASCI

ISSN：1672-6421

访问量0

下载量0

段落导航