铅酸电池失效模式和机理分析研究进展
Research progress of failure model and mechanism analysis of lead-acid battery
摘要
Abstract
The failure of the lead-acid battery (LAB) causes the capacity loss and short lifetime,even leads to serious energy and safety problems.The failure model and mechanisms research progress was reviewed,including positive active mass degradation and grid corrosion,irreversible formation of lead sulfate in negative plate,the impacts of high rate partial state of charge and temperature on irreversible sulfation,and the hydrogen evolution.关键词
铅酸电池/失效/不可逆硫酸盐化/HRPSoC/析氢Key words
lead-acid battery/failure model/irreversible sulfation/HRPSoC/hydrogen evolution分类
信息技术与安全科学引用本文复制引用
杨俊,胡晨,汪浩,刘晶冰,杨凯..铅酸电池失效模式和机理分析研究进展[J].电源技术,2018,42(3):459-462,4.基金项目