硅酸盐通报2018，Vol.37Issue(4)：1299-1302,1308,5.
P2O5含量对铝硅酸盐玻璃离子交换性能的影响
Effects of Phosphorus Pentoxide Content on Ion Exchange Performance of Aluminosilicate Glasses
摘要
Abstract
To investigate the effect of P2O5content on ion exchange performance of aluminosilicate glasses, glass samples were processed for ion-exchanging.Glass hardness, surface compressive stress (CS),element content change and ion-exchange depth were measured via micro hardness tester,surface stress meter, micro x ray fluorescence(micro-XRF)and field emission scanning electron microscopy (FESEM),respectively.The results showed that the K +content on glass surface increased apparently followed by decreasing of Na +.It was indicated that the ion exchange reaction was fully conducted at glass surface.Besides, the hardness, surface stress and ion-exchanged layer depth increased gradually with the addition of P2O5.The experiment results demonstrated that the introduction of P 2O5had a big effect on promoting the ion exchange reaction of aluminosilicate glass.关键词
离子交换/铝硅酸盐玻璃/P2O5含量Key words
ion-exchange/aluminosilicate glasses/P2O5content分类
化学化工引用本文复制引用
杨斌,汪玲,郭洋洋,陈建定,曾惠丹,陈国荣..P2O5含量对铝硅酸盐玻璃离子交换性能的影响[J].硅酸盐通报,2018,37(4):1299-1302,1308,5.基金项目
国家自然科学基金(21476083,51572082) （21476083,51572082）