印染助剂2018，Vol.35Issue(5)：33-38,6.
含氟聚倍半硅氧烷制备自修复疏水真丝织物
Preparation of self repairing hydrophobic silk fabric using fluorinated polysiloxane
李新玥 1李璐2
作者信息
- 1. 西安工程大学产业用纺织品协同创新中心,陕西西安 710048
- 2. 苏州大学纺织与服装工程学院,江苏苏州 215021
- 折叠
摘要
Abstract
The fluorinated polysiloxane (F-POSS) was synthesized. Silk fabrics were treated by F-POSS through rol ing and baking, and self repairing and hydrophobic properties of the silk fabrics were obtained. The effects of F-POSS concentration, polyacrylate concentration, pre-drying/baking temperature and time on the hydrophobicity of silk fabrics were discussed. The optimal process was as fol ows:F-POSS dosage 3 g/L, poly-acrylate dosage 100 g/L, 80 ℃ pre-drying 5 min, 140 ℃ baking 3 min. The self repair performance of self re-pairing hydrophobic silk fabrics after being destroyed was good. After the fabric had been rubbed, the surface damage and the partial loss of the low surface energy had little effect on the hydrophobicity and physical prop-erties, and the self-healing property of the fabric was good.关键词
自修复/疏水/真丝织物/含氟聚倍半硅氧烷Key words
self repairing/hydrophobic/silk fabrics/fluorinated polysiloxane分类
化学化工引用本文复制引用
李新玥,李璐..含氟聚倍半硅氧烷制备自修复疏水真丝织物[J].印染助剂,2018,35(5):33-38,6.