硅酸盐通报2018，Vol.37Issue(5)：1538-1542,5.
掺加热水解污泥制备水泥熟料的微观机理研究
Microcosmic Mechanism Research of Cement Clinker Prepared with Thermal Hydrolysis Sludge
摘要
Abstract
Cement clinker was prepared by adding different proportions of sludge ash .The influence of the clinker on the mineral and micro-structure of clinker was investigated by flammability test , diffraction, petrographic analysis, nuclear magnetic resonance etc .The results show that the content of f-CaO decreased first and then increased with the increase of sludge content .And the ratio of C3 S/C2 S lead to the reverse law by diffraction and nuclear magnetic resonance .The content of C3 S was the highest when the amount of sludge was one percent .At this percent, the crystalline type was complete and the mineral phases was well distributed through lithofacies analysis .The optimum content is one percent from mineral composition and microstructure.关键词
热水解污泥/水泥熟料/微观机理Key words
thermal hydrolysis sludge/cement clinker/microcosmic mechanism分类
化学化工引用本文复制引用
赵维,牟正平,范海宏,李斌斌..掺加热水解污泥制备水泥熟料的微观机理研究[J].硅酸盐通报,2018,37(5):1538-1542,5.基金项目
水体污染控制与治理科技重大专项(2010ZX07319-002) （2010ZX07319-002）