核级碳钢小径薄壁管冷弯拉伸试验不合格原因分析与质量控制措施
Failure Analysis and Quality Control Measures for the Cold Bending Tensile Test of Thin Wallpipe of Nuclear Grade Carbon Steel
贺振宇 1张强升 1张发云 1熊冬庆 1邓冬1
作者信息
- 1. 环境保护部核与辐射安全中心,北京 100082
- 折叠
摘要
Abstract
Thetension test resultof thin-walled tube after cold bendingis unqualified. Through the analysis of causes of tension test resultdata, includingraw material, cold bending, thickness and shape, measuring method and processing technical of test sample, confirm the reasonwhichthe tension test resultdata isunqualified. and re-tension test tothecold bending, adopt quality control measurefurther, ensured the tension test toachieve the requirementof standard.关键词
小径试验/原因分析/质量控制措施Key words
thin-walled tube/tensile test/causal analysis/quality control measures分类