吉林大学学报（医学版）2019，Vol.45Issue(1)：83-87,5.DOI:10.13481/j.1671-587x.20190116
3种玻璃陶瓷与Wieland Zenostar氧化锆相互摩擦的耐磨性比较
Comparison of wear resistance of three kinds of glass ceramics and Wieland Zenostar zircona
摘要
Abstract
Objective:To explore the differences of wear resistance of three kinds of glass ceramics and Wieland Zenostar zircona (Zenostar) , and to clarify their influencing factors.Methods:Zenostar were made into flat-shaped specimens (zirconia base sample group) and hemisphere-shaped specimens (zirconia pair grinding group) .There kinds of glass ceramics IPS Empress (Empress) , IPS e.max CAD (e.max) , VITA Suprinity (Suprinty) were used as base specimens.Each group was exposed to UMT-2testing machine to simulate the clinical service.The wear depthes of base specimens were detected by laser confocal scanning.Scanning electron microscope (SEM) was used to evaluate the wear surfaces.Results:In zirconia base sample group, there were no significant differences in the maximum wear depthes to Zenostar between the three kinds of glass ceramics (P＞0.05) .In zirconia pair grinding group, the maximum wear depthes ranked as follows:Zenostar group＜e.max group≈Empress group＜Suprinity group;there was no significant difference between e.max group and Empress group (P＞0.05) , but there were significant differences between other groups (P＜0.01) .The SEM results showed that the wearing surface of the Zenostar in zirconia base sample group was relatively smooth;whereas the wearing surface of Empress in zirconia pair grinding group was rougher with alarge area of clebris desquamation surface.Conclusion:The wear resistance of the three kinds of glass ceramics to Zenostar is related to the compositions and the chemical structures of materials.关键词
玻璃陶瓷/氧化锆/摩擦磨损/磨损深度Key words
glass ceramic/zirconia/friction and wear/wear depth分类
医药卫生引用本文复制引用
周园园,朱亚平,秦娇娇,李怡然,吴庆翠,王成坤,焦珊..3种玻璃陶瓷与Wieland Zenostar氧化锆相互摩擦的耐磨性比较[J].吉林大学学报（医学版）,2019,45(1):83-87,5.基金项目
吉林省科技厅科技发展计划项目资助课题(20140414010GH) （20140414010GH）