Internal shrinkage crack in a 10t water-cooled steel ingot with a large height-to-diameter ratio

Jing-an Yang Hou-fa Shen

中国铸造2021，Vol.18Issue(2)：110-117,8.

Internal shrinkage crack in a 10t water-cooled steel ingot with a large height-to-diameter ratio

Jing-an Yang ¹Hou-fa Shen²

作者信息

1. School of Transportation Science and Engineering, Beihang University, Beijing 100191, China
2. School of Materials Science and Engineering, Tsinghua University, Beijing 100084, China
折叠

摘要

关键词

steel ingot/porosity/hot crack/industrial CT/thermo-mechanical simulation

Key words

steel ingot/porosity/hot crack/industrial CT/thermo-mechanical simulation

分类

矿业与冶金

引用本文复制引用

Jing-an Yang,Hou-fa Shen..Internal shrinkage crack in a 10t water-cooled steel ingot with a large height-to-diameter ratio[J].中国铸造,2021,18(2):110-117,8.

基金项目

This work was financially supported by the NSFC-Liaoning Joint Fund(Grant No.U1508215)and the project"To Strengthen Industrial Development at the Grass-Roots Level of MIIT China"(Grant No.TC160A310/21).Additionally,assistance from the Special Material Institute of Inner Mongolia North Heavy Industries Group Co.,Ltd.is acknowledged. （Grant No.U1508215）

中国铸造

OASCI

ISSN：1672-6421

访问量0

下载量0

段落导航