TiN/γ-Fe interface orientation relationship and formation mechanism of TiN precipitates in Mn18Cr2 steel

Zheng-hui Wang Jing-pei Xie Qian Li Wen-yan Wang Ai-qin Wang Pei Liu

中国铸造2021，Vol.18Issue(3)：180-184,5.

TiN/γ-Fe interface orientation relationship and formation mechanism of TiN precipitates in Mn18Cr2 steel

Zheng-hui Wang ¹Jing-pei Xie ²Qian Li ³Wen-yan Wang ⁴Ai-qin Wang ¹Pei Liu²

作者信息

1. School of Materials Science and Engineering,Zhengzhou University,Zhengzhou 450001,China
2. National Center of International Research for Micro-nano Molding Technology,Zhengzhou University,Zhengzhou 450001,China
3. School of Materials Science and Engineering,Henan University of Science and Technology,Luoyang 471023,China
4. Provincial and Ministerial Co-construction of Collaborative Innovation Center for Non-ferrous Metal New Materials and Advanced Processing Technology,Henan University of Science and Technology,Luoyang 471023,China
折叠

摘要

关键词

Mn18Cr2 steel/TiN precipitates/interface orientation relationship/interface misfit

Key words

Mn18Cr2 steel/TiN precipitates/interface orientation relationship/interface misfit

分类

矿业与冶金

引用本文复制引用

Zheng-hui Wang,Jing-pei Xie,Qian Li,Wen-yan Wang,Ai-qin Wang,Pei Liu..TiN/γ-Fe interface orientation relationship and formation mechanism of TiN precipitates in Mn18Cr2 steel[J].中国铸造,2021,18(3):180-184,5.

基金项目

The authors acknowledge the financial support from the National Natural Science Foundation of China (Grant No. U1604251) and the Major Scientific and Technological Project of Luoyang, China (Grant No. 2001017A). （Grant No. U1604251）

中国铸造

OASCI

ISSN：1672-6421

访问量0

下载量0

段落导航