Effect of mold and core preheating temperature on corrosion resistance of casting Al-12Si alloy U-shaped cooling channel

Guang-long Li Jie Zhang Meng-yu Wang Rui-ming Su Yang Cao Ying-dong Qu

中国铸造2023，Vol.20Issue(3)：218-224,7.

Effect of mold and core preheating temperature on corrosion resistance of casting Al-12Si alloy U-shaped cooling channel

Guang-long Li ¹Jie Zhang ¹Meng-yu Wang ²Rui-ming Su ¹Yang Cao ¹Ying-dong Qu¹

作者信息

1. School of Materials Science and Engineering,Shenyang University of Technology,Shenyang 110870,China||Key Laboratory of Light Metal Materials and Engineering at Universities of Liaoning Province,Shenyang University of Technology,Shenyang 110870,China
2. School of Materials Science and Engineering,Shenyang University of Technology,Shenyang 110870,China
折叠

摘要

关键词

U-shaped cooling channels/roughness/exfoliation corrosion/intergranular corrosion

Key words

U-shaped cooling channels/roughness/exfoliation corrosion/intergranular corrosion

分类

矿业与冶金

引用本文复制引用

Guang-long Li,Jie Zhang,Meng-yu Wang,Rui-ming Su,Yang Cao,Ying-dong Qu..Effect of mold and core preheating temperature on corrosion resistance of casting Al-12Si alloy U-shaped cooling channel[J].中国铸造,2023,20(3):218-224,7.

基金项目

This research was financially supported by the National Natural Science Foundation of China(No.51775353),the&nbsp （No.51775353）

National Key Research and Development Program of China(No.2019YFB2006501),the Program for Natural Science Foundation of Liaoning Province(No.2021-BS-150),Science and Technology Program of Liaoning Provincial Department of Education(LJKZ0116),and Hebei Key Laboratory of Dielectric and Electrolyte Functional Material,Northeastern University at Qinhuangdao(HKDEFM2021204). （No.2019YFB2006501）

中国铸造

OACSCDCSTPCDEI

ISSN：1672-6421

访问量0

下载量0

段落导航