人工晶体学报2023，Vol.52Issue(12)：2215-2221,7.
AlON透明陶瓷的制备及其力学性能研究
Preparation and Mechanical Properties of AlON Transparent Ceramics
摘要
Abstract
AlON transparent ceramics have broad application prospects in national defense and civil use due to its good light transmission,thermal shock stability,mechanical properties and good processability.The AlON powder were prepared in batches by an improved carbothermal reduction nitridation/fluidized bed method in this article.A single batch can prepare up to 2 kg,and no second phase was observed in the XRD patterns of AlON powder.Laser particle size analysis shows an average particle size of 1.54 μm and the particle size distribution is uniform.Green body with good uniformity and high density was obtained using the powder molded by cold isostatic pressing.AlON transparent ceramics with transmissivity of 82.3%and bending strength of 310 MPa were prepared by sintering temperature at 1 850℃and nitrogen pressure of 5 MPa,which has certain practical significance for promoting the application of AlON transparent ceramics.关键词
AlON/碳热还原氮化法/高纯粉体/透明陶瓷/透过率/气压烧结Key words
AlON/carbothermal reduction nitridation method/high-purity powder/transparent ceramics/transmittance/gas pressure sintering分类
化学化工引用本文复制引用
王颖,张微,田庭燕,黄存新,王震,陈建荣,石爽爽..AlON透明陶瓷的制备及其力学性能研究[J].人工晶体学报,2023,52(12):2215-2221,7.基金项目
国家重点研发计划(2022YFB3705900) （2022YFB3705900）