现代纺织技术2024，Vol.32Issue(1)：90-99,10.DOI:10.19398/j.att.202306010
紫外老化对冻绿染丝织品结构及同位素的影响
Effect of ultraviolet aging on the structure and isotopes of rhamnus utilis-dyed silk fabrics
摘要
Abstract
The Silk Road is a bridge for political,economic and cultural exchanges between the East and West.Silk is composed of silk protein and silk glue protein.Silk protein,accounting for about 80％of the silk component,is mainly composed of 18 amino acids such as glycine,alanine,serine and tyrosine.Some amino acids in silk are easily photochemically interacted with ultraviolet light,resulting in embrittlement of the silk fabric.Silk artifacts are often not intact after excavation,which puts forward new requirements for origin tracing of silk artifacts.Stable isotope technology is a potential method for origin tracing of unknown objects and is gradually applied to trace textile artifacts.To trace the origin of silk fabrics by using isotope technology,it is necessary to figure out the influence of dyeing and aging on the isotopes of silk fabrics. Light has greatinfluence on the preservation of silk fabrics.In this study,silk fabrics were mordant-dyed with natural rhamnus utilis dyestuff and under UV accelerated photoaging for 5,10,15 d and 30 d to simulate the possible state of silk artifacts under UV lighting.Then they were dried at 50℃for one hour and stored in a sealed bag for further testing.The color differences of the samples were tested by a spectrophotometer.The microscopic morphology and mechanical properties of the samples were examined by scanning electron microscopy(SEM)and a universal material testing machine.The chemical structure of colored silk fabrics with different photo-aging times were tested by using fourier transform infrared spectroscopy(FTIR).And the amide Ⅲ region was fitted to obtain the relative content changes of secondary structures.Stable isotope ratios of silk fabrics with different degrees of photoaging were tested.On this basis,the morphological and structural changes of silk fibers under the influence of light aging and the changes of stable isotopes of silk fibers under the condition of ultraviolet light aging were analyzed to provide basic data for the traceability of silk cultural relics.The results show that UV aging had great influence on the morphology and structure of silk fabrics.UV aging induced a rapid decrease in the color difference of silk fabrics.The color difference of mordant-dyed silk fabrics changed most obviously.Cracks were shown in the surfaces of the aged silk fibers and the mechanical properties of the aged silk fabrics were greatly reduced,with the greatest reduction happening in rhamnus utilis-dyed samples.The β-sheet structure of the silk fibers was destroyed after aging.More heavy carbon isotopes were left in the aged silk fabrics compared with the control samples,especially for the mordant-dyed silk fabrics.关键词
冻绿/草木染/丝织品/紫外光老化/二级结构/稳定同位素Key words
rhamnus utilis/plant dyeing/silk fabric/ultraviolet aging/secondary structure/stable isotopes分类
轻工纺织引用本文复制引用
蔡逸岚,杨丹,贾丽玲,周旸,彭志勤..紫外老化对冻绿染丝织品结构及同位素的影响[J].现代纺织技术,2024,32(1):90-99,10.基金项目
国家重点研发计划项目(2023YFF0903800) （2023YFF0903800）
浙江省自然科学基金项目(LY19D030001) （LY19D030001）
浙江省文物局项目(2023001,2021015) （2023001,2021015）