云母片含量对三元乙丙橡胶性能的影响
Effect of Mica Sheet Content on Gas Barrier Characteristics of EPDM
摘要
Abstract
EPDM/mica sheet composites were prepared by using melt blending technology,EPDM rubber(EPDM)as the matrix material,tetramethylthiuram disulfide(TMTD)as the vulcanizing agent,zinc oxide,stearic acid(SA)and sulfur as the compounding agent,and mica flakes as fillers.Infrared and electron microscope scanning analysis were carried out on mica sheets.The mechanical properties,IR,SEM,TG,water contact angle,cross-linking density,water absorption and gas barrier properties of EPDM/mica sheet composites were tested.The effect of mica flake content on the properties of the composites was tested.The results show that when the content of mica sheet is 15.33％(wt.),the water absorption rate of the composite material reaches the lowest,and the water absorption rate is only 0.18％after immersion in boiling water for 12h.The gas barrier performance achieved the best effect,and the air permeability coefficient was only 1.345×10-10 cm2/(Pa·s),which was 71.1％lower than that of the blank EPDM vulcanized rubber without doped mica sheet.EPDM/mica sheet composites have good mechanical properties,thermal stability and gas barrier properties.关键词
三元乙丙橡胶/云母片/气体阻隔Key words
EPDM rubber/mica sheets/gas barrier分类
化学化工引用本文复制引用
樊玉瑞,张正国,孙友谊,雷青娟,刘奇超,刘子萱..云母片含量对三元乙丙橡胶性能的影响[J].合成材料老化与应用,2024,53(1):20-24,5.基金项目
山西省基础研究计划联合资助项目(太重)(TZLH20230818009)、山西省成果转化项目(202104021301059)、山西省科技创新团队专项基金(202204051001006)、阳泉市重点研发计划项目(2023JH055)资助. （太重）