塑料科技2024，Vol.52Issue(1)：59-62,4.DOI:10.15925/j.cnki.issn1005-3360.2024.01.013
低密度聚乙烯/热塑性弹性体的电缆阻燃材料的制备及其性能研究
Preparation and Property Study of Low Density Polyethylene/Thermoplastic Elastomer Flame Retardant Materials for Cables
摘要
Abstract
To enhance the flame retardancy of cable materials,a low density polyethylene/thermoplastic elastomer matrix(LDPE/TPE)was prepared,and flame-retardant materials such as modified aluminum hydroxide(ATH),microencapsulated red phosphorus(MRP),alumina(Al2O3),and organically modified silica(SiO2)were added to improve the properties of the composites under electron beam radiation crosslinking.The results show that with the increase of TPE component,the melt flow rate(MFR)of the blend initially increases and then decreases.When the TPE content is 28%,the MFR of the blend reaches its maximum at 5.93 g/10 min.A small additive amount of TPE can enhance the processing properties of the LDPE/TPE blend.When flame retardant materials are compounded and filled,with the addition of 50 parts ATH,30 parts MRP,30 parts Al2O3,and 10 parts organically modified SiO2,the comprehensive property of the composite is optimal.As the radiation dose increase,the gel content of the composite initially increases and then stabilizes.关键词
低密度聚乙烯/热塑性弹性体/辐射交联Key words
Low density polyethylene/Thermoplastic elastomer/Radiation crosslinking分类
通用工业技术引用本文复制引用
孔德忠..低密度聚乙烯/热塑性弹性体的电缆阻燃材料的制备及其性能研究[J].塑料科技,2024,52(1):59-62,4.基金项目
江苏省第六期"333高层次人才培养工程"资助(2022)3-16-828 （2022）
江苏省高等学校自然科学研究项目资助项目(19KJD430006) （19KJD430006）