The application of microwave heating technology in asphalt concrete pavement deicing has attracted much attention.However,the current approach often involves enhancing the entire asphalt pavement with microwave heating,leading to poor heating efficiency of the road surface.An ultra-thin microwave absorbing wear layer was prepared using silicon carbide(SiC)microwave enhanced aggregate to improve the microwave heating efficiency of road surface.The microwave heating efficiency and heating durability of ultra-thin microwave absorbing wear layer were investigated by microwave heating and deicing tests,and the optimum thickness of ultra-thin microwave absorbing wear layer was determined.The muti-physics microwave heating model established by COMSOL Multiphysics was used to analyze the influence of ultra-thin microwave absorbing wear layer on the intensity and distribution of electromagnetic field and temperature field during microwave heating.The results show that the ultra-thin microwave absorbing wear layer exhibits excellent microwave heating performance at a frequency of 2.45 GHz.The 10mm ultra-thin microwave absorbing wear layer has better microwave heating performance,and its temperature rate was 4.47 times and 1.40 times higher than that of the ordinary asphalt mixture and overall microwave-enhanced asphalt mixture.The stable microwave absorption property of SiC ensured that ultra-thin microwave absorbing wear layer had better microwave deicing durability,and the deicing time of ultra-thin microwave absorbing wear layer could still be maintained for about 45 s after repeated microwave heating.The numerical simulation results show that the strong microwave absorption capacity of the ultra-thin absorbing wear layer could partly enhance the electromagnetic field strength of the surface layer of the specimen,leading higher temperature on the surface of the specimen.The electric field intensity and magnetic field intensity inside the ultra-thin wave-absorbing wear layer increased by 50.9%and 15.7%,respectively,compared with ordinary asphalt mixture.In summary,it can be seen that the ultra-thin wave-absorbing wear layer can improve the microwave heating performance of asphalt pavement surface.关键词
沥青混凝土/微波加热/超薄吸波磨耗层/温升速率/多物理场Key words
asphalt concrete/microwave heating/ultra-thin microwave absorbing wear layer/heating rate/multi-physics field分类
建筑与水利引用本文复制引用
彭东黎,张细和,丁俊剑,刘小明,刘旭..多物理场下超薄吸波磨耗层微波加热性能研究[J].铁道科学与工程学报,2024,21(2):648-658,11.基金项目
国家自然科学基金资助项目(52078499) （52078499）
湖南省自然科学基金资助项目(2022JJ30730) （2022JJ30730）
湖南省交通科技项目(202246) （202246）