Oxidation behavior of 4774DD1 Ni-based single-crystal superalloy at 980℃ in airOACSTPCDEI
The oxidation behavior of a novel Ni-based single-crystal 4774DD1 superalloy for industrial gas turbine applications was investigated by the isothermal oxidation at 980℃ and discontinuous oxidation weight gain methods.The phase constitution and morphology of surface oxides and the characteristics of the crosssection oxide film were analyzed by XRD,SEM and EDS.Results show that the oxidation kinetics of the 4774DD1 superalloy follows the cubic law,indicating its weak oxidation resistance at this temperature.As the oxidation time increases,the composition of the oxide film evolves as following:One layer consisting of a bottom Al_(2)O_(3)sublayer and an upper(Al_(2)O_(3)+NiO)mixture sublayer after oxidized for 25 h.Then,two layers composed of an outermost small NiO discontinuous grain layer and an internal layer for 75 h.This internal layer is consisted of the bottom Al_(2)O_(3)sublayer,an intermediate narrow CrTaO_(4)sublayer,and an upper(Al_(2)O_(3)+NiO)mixture sublayer.Also two layers comprising an outermost relative continuous NiO layer with large grain size and an internal layer as the oxidation time increases to 125 h.This internal layer is composed of the upper(Al_(2)O_(3)+NiO)mixture sublayer,an intermediate continuous(CrTaO_(4)+NiWO_(4))mixture sublayer,and a bottom Al_(2)O_(3)sublayer.Finally,three layers consisting of an outermost(NiAl2O_(4)+NiCr2O_(4))mixture layer,an intermediate(CrTaO_(4)+NiWO_(4))mixture layer,and a bottom Al_(2)O_(3)layer for 200 h.
Yu Fang;Ya-zhou Li;Qiang Yang;Qun-gong He;Xiu-fang Gong;Qian Duan;Hai-yang Song;Fu Wang;Qiong-yuan Zhang;Hong Zeng;
State Key Laboratory of Long-Life High Temperature Materials,Dongfang Turbine Co.,Ltd.,Deyang 618000,Sichuan,ChinaState Key Laboratory for Manufacturing System Engineering,School of Mechanical Engineering,Xi’an Jiaotong University,Xi’an 710049,China
金属材料
nickel-base single crystal superalloyoxidation kineticsoxide filmmicrostructuremechanism
《China Foundry》 2024 (002)
P.116-124 / 9
supported by the fund of State Key Laboratory of Long-life High Temperature Materials(Grant No.DTCC28EE200787);the Natural Science Basic Research Plan in Shaanxi Province of China(Grant No.2022JQ-553);the China Postdoctoral Science Foundation(Grant No.2021M692555);the Excellent Youth Foundation of Shaanxi Province of China(Grant No.2021JC-08);the Beilin district of Xi’an Science and Technology Project(Grant No.GX2123);the support from the Youth Innovation Team of Shaanxi Universities。