理化检验-物理分册2024，Vol.60Issue(2)：13-16,4.DOI:10.11973/lhjy-wl202402004
FeCrAl合金显微组织腐蚀方法比较
Comparison of FeCrAl alloy microstructure erosion methods
曹萍 1陈涛 2潘佳燕1
作者信息
- 1. 浙江久立特材科技股份有限公司, 湖州 313008||浙江省核电用高性能管材成形工程技术研究中心, 湖州 313008
- 2. 浙江久立特材科技股份有限公司, 湖州 313008
- 折叠
摘要
Abstract
The effects of four different erosion methods on FeCrAl alloy were compared and analyzed by optical microscope and scanning electron microscope.The results show that the grain morphology of FeCrAl alloy could be obviously observed by three chemical erosion methods with 10 g ferric chloride+30 mL hydrochloric acid+ 120 mL distilled water,the volume fraction ratio of HF,HNO3 and H2O was 1∶10∶50,and the volume fraction ratio of HCl and H2O was 1∶3.The thermal erosion method of HCl and H2O mixed solution was preferred,the microstructure of the alloy obtained by this method had no interference of grain boundary and grain brightness,and the grain size rating photo was clearer.The erosion method of 10 g ferric chloride+30 mL hydrochloric acid+ 120 mL distilled water could be used to observe and analyze the grain boundary.The erosion method with the volume fraction ratio of HF,HNO3 and H2O of 1∶10∶50 could be used for the observation and analysis of the second phase.关键词
FeCrAl合金/制备试样/显微组织/腐蚀方法/金相检验Key words
FeCrAl alloy/preparing sample/microstructure/erosion method/metallographic examination分类
矿业与冶金引用本文复制引用
曹萍,陈涛,潘佳燕..FeCrAl合金显微组织腐蚀方法比较[J].理化检验-物理分册,2024,60(2):13-16,4.