镀锌板表面翘皮类缺陷产生原因
Causes of warping defects on the surface of galvanized sheet
刘向明 1王伟 1陈立平 1侯永亮 1王勇1
作者信息
- 1. 首钢京唐钢铁联合有限责任公司, 唐山 063200
- 折叠
摘要
Abstract
Aiming at three kinds of typical warping defects in a hot-dip galvanizing production line,the surface morphology and matrix structure of the defects were analyzed by scanning electron microscope,and the composition of the surface and cross section of the defects was analyzed by energy dispersive spectrometer,and then the process of the defects was identified.The results show that there were reduced iron oxide on the surface of No.1 sample,iron oxide and a large number of oxidation dots on the cross section,and high temperature welding in some warping areas,the dots were caused by the surface defects of the slab inherited to the subsequent process.There was reduced iron oxide on the surface of No.2 sample,iron oxide on the cross section,and high temperature welding in some warping areas,the dots were produced by hot rolling process.There was no iron oxide and oxide dots in sample 3,the warping defects were produced in the cold state.关键词
翘皮缺陷/氧化圆点/缺陷/镀锌板/氧化铁Key words
warping defect/oxidation dot/defect/galvanized plate/iron oxide分类
通用工业技术引用本文复制引用
刘向明,王伟,陈立平,侯永亮,王勇..镀锌板表面翘皮类缺陷产生原因[J].理化检验-物理分册,2024,60(2):47-50,4.