理化检验-物理分册2024，Vol.60Issue(2)：56-59,4.DOI:10.11973/lhjy-wl202402015
35CrMo钢蓄能器开裂原因
Cracking reason of 35CrMo steel accumulator
聂志川1
作者信息
- 1. 辽宁省本溪市产品质量监督检验所, 本溪 117000
- 折叠
摘要
Abstract
The accumulator produced by a company cracked after one year of use.The cracking reason of the accumulator was analyzed by means of macroscopic observation,chemical composition analysis,mechanical property test,scanning electron microscope analysis and metallographic examination.The results show that there were microcracks in 35CrMo steel which was used to make the accumulator shell.When the accumulator was working,the pressure generated by the internal medium gas and hydraulic oil caused the micro cracks to gradually expand and penetrate the pipe wall,resulting in the accumulator cracking.关键词
35CrMo钢/非金属夹杂物/晶粒度/调质处理/穿孔Key words
35CrMo steel/non-metallic inclusion/grain size/quenching and tempering treatment/perforation分类
矿业与冶金引用本文复制引用
聂志川..35CrMo钢蓄能器开裂原因[J].理化检验-物理分册,2024,60(2):56-59,4.