理化检验-物理分册2024，Vol.60Issue(3)：75-78,4.DOI:10.11973/lhjy-wl202403019
45Mn2钢圆管开裂原因
Reason for cracking of 45Mn2 steel circular tube
鞠海兵 1秦小梅 1赵亚娟1
作者信息
- 1. 南京钢铁股份有限公司, 南京 210035
- 折叠
摘要
Abstract
Cracks were found on the surface of a 45Mn2 steel billet processed into a circular tube.The cause of surface cracking of steel pipes was analyzed using methods such as macroscopic observation,chemical composition analysis,microscopic analysis,and electron probe microanalysis.The results show that the abnormal metal did not fuse with the substrate,and during the grinding treatment of the steel tube,the abnormal metal experienced detachment.The structure and chemical composition of the abnormal metal were different from those of the substrate.Different metals were pressed into the surface of the steel tube,causing cracking on the surface of the steel tube.关键词
45Mn2钢/开裂/异常金属/电子探针显微分析/显微组织/脱碳Key words
45Mn2 steel/cracking/abnormal metal/electron probe microanalysis/microstructure/decarbonization分类
矿业与冶金引用本文复制引用
鞠海兵,秦小梅,赵亚娟..45Mn2钢圆管开裂原因[J].理化检验-物理分册,2024,60(3):75-78,4.