SnS2/SnS/NC异质结构微米花的构筑及储钾性能探究OACSTPCD
Construction and K-ion Storage Properties of SnS2/SnS/NC Heterostructures Micro-flowers
采用水热法制备SnS2 微米花(MFs),以聚多巴胺衍生的氮掺杂碳(NC)作为还原剂和缓冲基质,合成了SnS2/SnS/NC异质结构微米花(SSNC MFs)作为钾离子电池负极材料.SnS2 和SnS形成的异质界面加快了电荷的转移,进而改善了电化学动力学.同时,NC增强了复合材料的导电性和结构稳定性.因而,SSNC MFs电极在0.1 A/g下,循环50周的可逆比容量为492.4 mAh/g,2.0 A/g下仍保持在199.6 mAh/g,远大于相同测试条件下的SnS2MFs电极(分别为132.1和28.4 mAh/g),表现出显著提升的可逆比容量、循环稳定性和倍率性能.
SnS2 micro-flowers(MFs)were synthesized by hydrothermal,and then SnS2/SnS/NC heterostructures micro-flowers(SSNC MFs)were constructed by PDA-derived carbon as reducing agent and buffer substrate.SSNC MFs was evaluated as KIBs anode material,the interfaces of SnS2/Sn heterostructures facilitate the charge transfer and further improve the kinetics.Meanwhile,the nitrogen-doped carbon layer improved the conductivity and structural stability of the hybrid electrode.As a result,the as-prepared SSNC MFs electrode exhibits improved specific capacity,cycle stability and rate performance.It delivered the reversible capacity of 492.4 mAh/g at 0.1 A/g after 50 cycles and 199.6 mAh/g was remained at 2.0 A/g,which was much higher than that of the SnS2 MFs electrode(132.1 mAh/g and 28.4 mAh/g at the same condition,respectively).
曹康哲;何亚楠;王思甜;付金金;刘会俏
信阳师范大学 化学化工学院/信阳市低碳能源材料重点实验室,河南 信阳 464000信阳师范大学 化学化工学院/信阳市低碳能源材料重点实验室,河南 信阳 464000信阳师范大学 化学化工学院/信阳市低碳能源材料重点实验室,河南 信阳 464000信阳师范大学 化学化工学院/信阳市低碳能源材料重点实验室,河南 信阳 464000信阳师范大学 化学化工学院/信阳市低碳能源材料重点实验室,河南 信阳 464000
动力与电气工程
钾离子电池负极材料锡基硫化物异质结构储钾性能
K-ion batteryanode materialstin sulfidesheterostructureK-ion storage property
《信阳师范学院学报（自然科学版）》 2024 (2)