中国药房2024，Vol.35Issue(8)：925-930,6.DOI:10.6039/j.issn.1001-0408.2024.08.05
叶酸修饰的粉防己碱壳聚糖-硬脂酸纳米胶束的制备、表征及体外抗炎活性考察
Preparation,characterization and in vitro anti-inflammatory activity of tetrandrine-loaded chitosan-stearic acid nano micelles modified with folic acid
摘要
Abstract
OBJECTIVE To prepare tetrandrine(TET)-loaded chitosan(CS)-stearic acid(SA)nano micelles modified with folic acid(FA)(FA-CS-SA/TET nano micelles),characterize them and study the anti-inflammatory effect in vitro.METHODS FA-CS-SA/TET nano micelles were prepared by ultrasonic method;the preparation technology was optimized by orthogonal test and validation test was also performed with the mass ratio of FA-CS-SA to TET,ultrasound power and ultrasound times as the factors,using the comprehensive score of entrapment efficiency(EE),drug loading(DL)and particle size as evaluation index.FA-CS-SA/TET nano micelles prepared by the optimal technology were characterized,and their release performance in vitro was investigated.RAW264.7 cells were used as subjects to investigate their anti-inflammatory activity in vitro.RESULTS The optimal preparation technology included that the mass ratio of FA-CS-SA to TET was 2∶1,ultrasonic power was 200 W,and the ultrasonic frequency was 200 times.The parameters of FA-CS-SA/TET nano micelles prepared by optimized technology included that EE was(98.86±0.30)%,DL was(28.57±0.34)%,the average particle size was(227.0±9.4)nm,polydispersity index was 0.42±0.04,and the Zeta potential was(12.6±2.3)mV,respectively.The nano micelles were uniform in appearance and round in shape.The nano micelles were released quickly in 0.5%sodium dodecyl sulfate solution,with a cumulative release rate of(79.49±3.43)%within 72 hours,and its anti-inflammatory effect was stronger than that of TET raw materials.CONCLUSIONS FA-CS-SA/TET nano micelles are prepared successfully in the study,with good drug loading performance,uniform particle size,and good in vitro anti-inflammatory activity.关键词
粉防己碱/纳米胶束/制备工艺/表征/抗炎活性/释放度Key words
tetrandrine/nano micelles/preparation techno-logy/characterization/anti-inflammatory activity/release rate分类
医药卫生引用本文复制引用
薛飞,杨岚,常金花,刘沛,王汝兴..叶酸修饰的粉防己碱壳聚糖-硬脂酸纳米胶束的制备、表征及体外抗炎活性考察[J].中国药房,2024,35(8):925-930,6.基金项目
河北省自然科学基金项目(No.H2022406073) （No.H2022406073）
河北省高等学校科学技术研究重点项目(No.ZD2021004) （No.ZD2021004）
承德医学院高层次人才科研启动基金项目(No.201705) （No.201705）