云南化工2024，Vol.51Issue(4)：70-74,5.DOI:10.3969/j.issn.1004-275X.2024.04.15
Q345R在不同环境下的腐蚀行为研究
Research on Corrosion Behavior of Q345R in Different Environments
张露1
作者信息
- 1. 中铁第一勘察设计院集团有限公司,陕西 西安 710043
- 折叠
摘要
Abstract
The corrosion behavior of Q345R steel at different temperatures,CO2 and H2S partial pressure ratios was simulated by hightempera-ture and highpressure reactor and electrochemical workstation.The results show that the average corrosion rate increases as the temperature in-creases.At the temperature of 20℃ and 50℃,both CO2 and H2S have greater solubility,and the solution has a lower pH value,therefore,with the increase of CO2/H2S concentration,the uniform corrosion rate of Q345R steel increases significantly.The results of microscopic morphology and XRD analysis showed that H2S corrosion was dominant.关键词
Q345R/温度/CO2/H2SKey words
Q345 R/Temperature/CO2/H2 S分类
矿业与冶金引用本文复制引用
张露..Q345R在不同环境下的腐蚀行为研究[J].云南化工,2024,51(4):70-74,5.