摘要
Abstract
PP/PE/TiO2composite fibers were prepared by melt blending of polyethylene(PE),polypropylene(PP)and titanium dioxide nanoparticles(TiO2).The effects of TiO2 content on the structure,dynamic and mechanical properties of the composite fibers and photocatalytic degradation properties were investigated.The results showed that TiO2is uniformly dispersed in the composite fiber matrix as micro-aggregates,and the aggregate size increased with the increase of TiO2 content.The addition of TiO2 had no significant effect on the melting temperature(Tm)of the composite fibers,and a small amount of TiO2 had the effect of promoting nucleation,increasing the crystallization rate and increasing the crystallinity.With the increase of TiO2content,the breaking strength and knotting strength of the composite fibers first increased and then decreased,and a small amount of TiO2 had the effects of strengthening and toughening the composite fibers.After photodegradation for 200 h,the breaking strength of the composite fibers,the nodule strength loss rate and the TiO2 content tended to be linear.With the increase of TiO2content,the mechanical properties of the composite fibers decreased significantly,the breaking strength and knotting strength loss rate in-creased significantly,and the photodegradation performance was enhanced.[Chinese Fishery Quality and Standards,2024,14(2):28-34]关键词
聚乙烯/复合纤维/二氧化钛/接枝改性/结构性能Key words
polyethylene/composite fiber/titanium dioxide/graft modification/structural properties分类
农业科技