硅酸盐通报2024，Vol.43Issue(6)：2012-2021,10.
不同环境溶液下高吸水树脂对水泥基材料的裂缝修复性
Crack Repairability of Cementitious Materials by Superabsorbent Polymers in Different Environmental Solutions
摘要
Abstract
Cracking and repair of concrete have always been the focus of attention in engineering field.Superabsorbent polymers(SAP)have a certain crack self-healing function.In this paper,the liquid absorption properties of SAP under different environmental solutions(NaOH,NaCl and distilled water)were tested.The compressive strength recovery rate of cracked specimens,the self-healing rate of different crack widths(0.1,0.2 mm)and the crack filling state were used as repair indicators.The repair effect of SAP with different mass fractions(0％,0.5％,1.0％)on cracked mortar specimens under different environmental solutions was analyzed.The results show that the liquid absorption rate of SAP in different environmental solutions increases rapidly and then tends to be stable,and the liquid absorption rate of SAP in NaOH environmental solution is the highest.The incorporation of SAP improves the compressive strength recovery rate of cracked mortar specimens under different environmental solutions to a certain extent.Among them,the compressive strength recovery rate of specimens mixed with 0.5％SAP in NaOH environmental solution for 28 d is the highest,which is 17％higher than that of reference group.The incorporation of SAP improves the self-healing properties of mortar specimens with different crack widths in different environmental solutions.With the increase of SAP content,the self-healing properties of mortar specimens with 0.2 mm crack width repaired in NaOH environmental solution for 28 d is significantly higher than that of distilled water and NaCl solution.The self-healing rate of specimens with 1.0％SAP in NaOH environmental solution is 90％.The incorporation of SAP cooperates with hydration products to seal the crack mouth,so it is beneficial to improve the durability of cement mortar.关键词
环境溶液/高吸水树脂/砂浆/裂缝/抗压强度/自愈合Key words
environmental solution/superabsorbent polymer/mortar/crack/compressive strength/self-healing分类
建筑与水利引用本文复制引用
杨世界,张士萍,牛龙龙,张守卫..不同环境溶液下高吸水树脂对水泥基材料的裂缝修复性[J].硅酸盐通报,2024,43(6):2012-2021,10.基金项目
国家自然科学基金(52078247,51678292) （52078247,51678292）