新型细化剂Al-5Ti-1B-7Sm对7050合金显微组织及力学性能影响
Effect of the new refiner Al-5Ti-1B-7Sm on the properties of 7050 alloy
万里 1翟凤龙1
作者信息
- 1. 黑龙江科技大学,黑龙江 哈尔滨 150022
- 折叠
摘要
Abstract
s:This study investigates the effect of Al-5Ti-1B-7Sm refiner on the microstructure and mechanical properties of 7050 alloy.Experiments show that Al-5Ti-B-7Sm refiner is mainly composed of Ti2Al20Sm and TiB2 phases,and contains a very small amount of TiAl3.In 7050 alloy,the optimal amount of refiner added was 0.6%,the average grain size was reduced from 120.9μm before refinement to 66.9μm,and the ultimate tensile strength of cast alloy was increased from 120MPa to 141MPa.Fine-grain strengthening is the main reason why Al-5Ti-1B-7Sm refiner improves the strength of 7050 alloy.关键词
7050合金/细化剂/显微组织/力学性能Key words
7050 Alloy/Refiners/Microstructure/Mechanical properties分类
矿业与冶金引用本文复制引用
万里,翟凤龙..新型细化剂Al-5Ti-1B-7Sm对7050合金显微组织及力学性能影响[J].世界有色金属,2024,(7):7-9,3.