新型改性水玻璃固沙剂制备与研究
Preparation and Study of a New Modified Water-Glass Sand-Fixing Agent
摘要
Abstract
In order to solve the issues of relatively poor water resistance and unsatisfactory sand-fixing effect of existing chemical sand-fixing agents in the market,some organic and inorganic modified materials were added into water glass,a new type of composite sand-fixing agent with high strength,durability and stability was prepared.The results show that:a)According to the modulus of sodium silicate is 3.0,the addition of sodium tetraborate,lithium carbonate,sorbitol and polyacrylamide are 1.5%,2.5%,0.2%and 0.3%respectively,and the addi-tion of sodium carboxymethyl cellulose is 0.3%,the strength of the sand-fixing layer can reach 14.1 MPa.b)The new modified sodium sili-cate sand-fixing agent has good stability and durability.After aging at 70℃high temperature and-20℃low temperature for 7 days,the loss rates of unconfined compressive strength are 11.8%and 19.5%respectively,at 700℃,the mass loss rate is only 8.6%.c)The sand-fixing effect of the new modified sodium silicate sand-fixing agent is good.The sand-fixing layer shows no or slight wind erosion when the wind speed is less than 20 m/s.关键词
化学固沙剂/水玻璃/改性剂/抗压强度/风蚀率Key words
chemical sand-fixing agent/water-glass/modifier/compressive strength/wind erosion rate分类
资源环境引用本文复制引用
李凯崇,薛春晓,杨柳..新型改性水玻璃固沙剂制备与研究[J].人民黄河,2024,46(7):119-123,147,6.基金项目
甘肃省2016年工业转型升级专项资金资助项目(甘财经[2016]212号) （甘财经[2016]212号）