宇航材料工艺2024，Vol.54Issue(3)：38-44,7.DOI:10.12044/j.issn.1007-2330.2024.03.005
基于湿热环境下的碳纤维复合材料力学性能研究及老化寿命预测
Mechanical Properties Research and Aging Life Prediction of Carbon Fiber Composites Under Hygrothermal Environment
卢东滨 1刘欢 1马英杰 1李成建 1徐晋伟1
作者信息
- 1. 北京玻钢院复合材料有限公司,北京 102101
- 折叠
摘要
Abstract
T700/TDE-86 carbon fiber reinforced composites were subjected to artificial accelerated hygrothermal aging experiments.By comparing and analyzing the cross-sectional morphology and physical and chemical properties of the composite before and after aging,the moisture absorption and diffusion behavior of the composites were discussed,and the evolution law of the mechanical properties of composites was studied.The residual strength calculation model was constructed,and aging life of the composite in the hygrothermal environment was predicted by combining with the environmental coefficient.The results showed that the moisture absorption rate of the composite gradually increased until it turned flat with prolongation of aging time,which conformed to Fick's diffusion law.Compared with composite without the hygrothermal aging,the mechanical properties of aged composite decreased under 60℃ and 95％RH,among which the shear strength was the most serious,up to 25％after 64 days of aging.The life of T700/TDE-86 carbon fiber reinforced composites estimated based on residual strength and environmental coefficients was about 30 years,laying a foundation for determining the future service reliability of resin-based composites.关键词
碳纤维复合材料/湿热老化/力学性能/寿命预测Key words
Carbon fiber reinforced composite/The hygrothermal aging/Mechanical properties/Life prediction分类
通用工业技术引用本文复制引用
卢东滨,刘欢,马英杰,李成建,徐晋伟..基于湿热环境下的碳纤维复合材料力学性能研究及老化寿命预测[J].宇航材料工艺,2024,54(3):38-44,7.