R95钢级外加厚油管断裂失效分析
Analysis of Fracture Failure of R95 Externally-upset Tubing
纪然 1饶攀攀 1崔毅1
作者信息
- 1. 中国石油物资沧州有限公司,河北 沧州 061000
- 折叠
摘要
Abstract
Analyzed here in the paper are the causes for the fracture failure of a certain piece of tubing that has been used for three years.The following facts concerning the failure are revealed via the analysis.The failure tubing is loaded with the tensile stress along the longitudinal direction of the pipe body;so much S2-is found in the blowout liquid as collected on the operation site;and moreover the material of the R95 tubing itself has the SSC-caused fracture sensitive characteristic.As a result,the combined effects by the above mentioned three elements leads to the SSC fracture of the tubing.On the other hand the tubing's measured strength and hardness via the hardness test are rather high,and in general along with the increases of the strength and the hardness,the SSC fracture sensitivity of the material is getting higher and higher.Conclusively speaking,all the elements as mentioned here get the SSC fracture risk increased.Accordingly it is suggested to select as far as possible specialty tubular goods for service under acidic conditions,and to improve the quality control of the tubular goods as used under the acid conditions.关键词
油管/R95/外加厚/断裂/失效Key words
tubing/R95/externally-upset/fracture/failure引用本文复制引用
纪然,饶攀攀,崔毅..R95钢级外加厚油管断裂失效分析[J].钢管,2024,53(4):71-74,4.