830E卡车车架开裂原因分析及修复工艺
Causes analysis and repair technology for cracking of 830E truck frame
高磊1
作者信息
- 1. 国能准能集团有限责任公司 设备维修中心,内蒙古 鄂尔多斯 010300
- 折叠
摘要
Abstract
In order to solve the problem of cracking of the main beam of 830E truck frame,the article analyzes the stress situation of 830E truck frame structure under different working conditions.We cut and sample the cracked parts of the material,observe and analyze them under an electron microscope,and conduct tensile and cold bending experiments to identify the cause of the frame cracking.Based on the location,size,and stress concentration of the frame cracking,a targeted repair process was designed and successfully applied in practice.The results show that the repair technology can solve the problem of cracking in the concentrated parts of 830E truck,and the repair effect is good,which greatly extend the service life of the frame and improve the vehicle's output rate.关键词
830E车架/受力分析/开裂原因/焊接工艺/车架使用寿命Key words
830E frame/force analysis/cause of cracking/welding process/service life of frame分类
矿业与冶金引用本文复制引用
高磊..830E卡车车架开裂原因分析及修复工艺[J].露天采矿技术,2024,39(6):90-93,4.