粉末冶金技术2024，Vol.42Issue(6)：609-620,12.DOI:10.19591/j.cnki.cn11-1974/tf.2022090006
超细类球形钴粉的可控制备及调控机理
Controllable preparation and regulation mechanism of ultrafine spherical cobalt powders
摘要
Abstract
The CoCO3 precursors with fine,uniform,and controllable particle size were prepared by liquid-phase precipitation method,using CoCl2·6H2O and NH4HCO3 as raw materials,and then the ultrafine spherical cobalt powders were prepared by calcination-hydrogen reduction.The influence of stirring time and reaction temperature on the particle size and morphology of CoCO3 precursors in the liquid-phase precipitation method was analyzed,and the effect of reduction temperature and reduction time on the phase,particle size,and microstructure of the reduction products was investigated.The results show that the nucleation rate of CoCO3 precursors increases with the increase of stirring time and reaction temperature,and then the average particle size of CoCO3 decreases.The CoCO3 precursors with uniform particle size,high sphericity,and average particle size of 0.96 μm are prepared,when the stirring time is 45 min and the reaction temperature is 25℃.In the hydrogen reduction,the particle size of cobalt powders increases with the increase of hydrogen reduction time and temperature.When the hydrogen reduction temperature is 400℃for 45 min,the cobalt powders show the good dispersion and uniform particle size with the average particle size of 0.4 μm.关键词
液相沉淀法/碳酸钴前驱体/氢还原/类球形钴粉/粒径/形貌Key words
liquid phase precipitation/cobalt carbonate precursor/hydrogen reduction/spherical cobalt powders/particle size/morphology分类
矿业与冶金引用本文复制引用
刘柏雄,黄少勇,刘智平,赵文敏..超细类球形钴粉的可控制备及调控机理[J].粉末冶金技术,2024,42(6):609-620,12.基金项目