中国塑料2025，Vol.39Issue(3)：12-18,7.DOI:10.19491/j.issn.1001-9278.2025.03.003
具有优异力学性能的钛白粉增白GFRPA复合材料的制备及性能研究
Preparation and properties of TiO2-whitening PA6/GF composites with excellent mechanical performance
张衡 1刘浩 2邱守季 3张炳 4吴叔青1
作者信息
- 1. 华南理工大学材料科学与工程学院,广州 510640
- 2. 华南理工大学机械与汽车工程学院,广州 510640
- 3. 广州华新科智造技术有限公司,广州 510663
- 4. 中信钛业股份有限公司,辽宁 锦州 121005
- 折叠
摘要
Abstract
In this article,TiO2 was surface modified by macromolecular polybasic acid(BA)and lauric acid(LA)and then used to whiten the PA6/GF composites through extrusion molding.The effect of modified TiO2 on the crystalliza-tion behavior and interfacial and mechanical properties of the composites were investigated.The results indicated that there was no significant influence on the improvement of mechanical properties of PA6/GF composites at an LA-modi-fied TiO2 content of 3 wt.%.However,the composites with BA-modified TiO2 obtained tensile strength,flexural strength and notched impact strength of 109 MPa,155 MPa,and 12.3 kJ/m2,respectively,which were higher than those of the composites with pure TiO2 by 11.1%,10.7%,and 68.5%,respectively.All parameters reached 85%or more of the results for the composite systems with the same amount of ZnS.关键词
聚酰胺6/玻璃纤维/钛白粉/表面改性/冲击强度Key words
polyamide 6/glass fiber/titanium oxide/surface modification/impact strength分类
化学工程引用本文复制引用
张衡,刘浩,邱守季,张炳,吴叔青..具有优异力学性能的钛白粉增白GFRPA复合材料的制备及性能研究[J].中国塑料,2025,39(3):12-18,7.