棉纺织技术2025，Vol.53Issue(4)：72-75,4.
超细特腈纶莫代尔羊绒纤维混纺纱生产实践
Production practice of superfine acrylic Modal cashmere fiber blended yarn
张书峰 1宋均宜 1何亿 2曹凯 2王荣武2
作者信息
- 1. 山东联润新材料科技有限公司,山东 枣庄,277100
- 2. 东华大学纺织学院,上海,201620
- 折叠
摘要
Abstract
In order to develop fine and soft yarn,the siro-compact spinning was used to process superfine acrylic Modal cashmere fiber 50/40/10 blended yarn with linear density of 10 tex.The production key points,difficulties and corresponding solution measures in each process were discussed,the process parameters were optimized according to production practice.By preblending cashmere and Modal fiber,the mixing uniformity of small proportion cashmere fiber was improved by layering feeding.By making targeted modifications to FA036 mixed opening cotton machine in the carding process,impact on fiber was reduced and fiber damage was decreased.In carding process,the movable flat system was transformed into a fully fixed flat system with cotton net cleaning system,which was used to achieve the purpose of flexible carding.The results showed that breaking strength of the blended yarn was 18.2 cN/tex,twist factor of the yarn was 113.2 twists/10 cm,the yarn was soft,3 mm hairines of the yarn was 3.54 roots/10 m and the fabric had excellent breathability,air permeability of the fabric was 682 mm/s.关键词
羊绒纤维/超细特纤维/混纺纱/赛络集聚纺/工艺参数Key words
cashmere fiber/superfine fiber/blended yarn/siro-compact spinning/process parameter分类
轻工纺织引用本文复制引用
张书峰,宋均宜,何亿,曹凯,王荣武..超细特腈纶莫代尔羊绒纤维混纺纱生产实践[J].棉纺织技术,2025,53(4):72-75,4.