宿州学院学报2025，Vol.40Issue(3)：24-28,5.DOI:10.3969/j.issn.1673-2006.2025.03.005
硫化锌微米材料的制备及其光催化降解亚甲基蓝性能研究
Preparation of Zinc Sulfide Micro Materials and Their Photocatalytic Degradation Performance of Methylene Blue
摘要
Abstract
The Zinc sulfide(ZnS)sample was synthesized using Zinc acetate dihydrate,and thiourea as ingredients by the hydrothermal reaction without using any dispersants and surfactants were used in the reaction process.The product composition and morphology were confirmed by XRD and SEM.The experimental results showed that after hydrothermal reaction at 150℃for 12 h,the as-obtained ZnS microspheres diameter was about 4 μm.Then,ZnS microspheres were used as photocatalyst,and the photocatalytic degradation rate of methylene blue solution reached 91.1%after ultraviolet light irradiation for 150 min.关键词
硫化锌/水热法/光催化/亚甲基蓝Key words
ZnS/hydrothermal method/photocatalysis/methylene blue分类
化学化工引用本文复制引用
耿涛,张嘉辉,陈明康..硫化锌微米材料的制备及其光催化降解亚甲基蓝性能研究[J].宿州学院学报,2025,40(3):24-28,5.基金项目
宿州学院重点项目(2023yzd11) （2023yzd11）
安徽省大学生创新创业训练计划项目(S202310379171). （S202310379171）