宇航材料工艺2025，Vol.55Issue(2)：59-65,7.DOI:10.12044/j.issn.1007-2330.2025.02.008
热轧工艺对TA5板材组织及性能的影响
Effect of Hot Rolling Process on Microstructure and Performance of TA5 Plate
张野 1王安国 2宿纯文 2张薇 3戴山1
作者信息
- 1. 中铝沈阳有色金属加工有限公司,沈阳 110117
- 2. 沈阳航空航天大学,沈阳 110136
- 3. 沈阳飞机工业(集团)有限公司,沈阳 110086
- 折叠
摘要
Abstract
Through comparative analysis of microstructural properties of sheets processed via different hot working processes while avoiding cold rolling,an optimal process scheme was developed to address the poor matching between mechanical properties and bending formability of 4.0 mm TA5 sheets,thereby facilitating high-quality industrial mass production.The research indicates that β-quenching combined with warm rolling at 550℃ can rapidly refine slab microstructure by introducing multi-dislocations and substructures,effectively enhancing sample strength.For samples without β-quenching treatment,elongation and bending performance exhibit upward trends,showing a fundamentally positive correlation between bending formability and elongation.When TA5 ingots undergo hot breakdown rolling in the single-phase region to 9 mm,followed by 940℃ rolling to 5 mm,then warm rolling at 550℃ from 5 mm to 4 mm,and finally 650℃ annealing for 40minutes with air cooling,uniform fine equiaxed microstructures can be achieved.关键词
TA5板材/热轧/组织/性能/折弯Key words
TA5 sheet/Hot rolling/Tissue/Property/Bend分类
金属材料引用本文复制引用
张野,王安国,宿纯文,张薇,戴山..热轧工艺对TA5板材组织及性能的影响[J].宇航材料工艺,2025,55(2):59-65,7.