包装学报2025，Vol.17Issue(3)：62-68,7.DOI:10.20269/j.cnki.1674-7100.2025.3008
尼龙6原位包覆碳纤维布的制备
Preparation of PA6 In-Situ Covered Carbon Fiber Cloth
摘要
Abstract
In this study,N,N dimethylformamide(DMF)impregnation and high-temperature calcination were used to remove the epoxy sizing agent on the surface of commercial carbon fiber cloth(CFC),followed by γ-aminopropyltriethoxysilane(KH550)surface modification of the treated CFC,and then finally anionic in-situ polymerization was used to prepare the composite of nylon 6(PA6)in-situ coated carbon fiber cloth.Scanning electron microscopy(SEM),Fourier transform infrared spectroscopy(FTIR),X-ray photoelectron spectroscopy(XPS),and thermogravimetic analysis(TGA)were used to characterize the carbon fiber cloth before and after treatment and the composites of PA6 in-situ-coated carbon fiber cloth,while the effects of the removal method,the surface modification of the carbon fiber cloth by KH550,and anionic in-situ polymerization on the PA6-coated carbon fiber cloth were investigated.The results showed that DMF impregnation while high-temperature calcination treatment could effectively remove the epoxy resin on the surface of commercial carbon fiber cloth,but the effect of high-temperature calcination treatment was significantly better than that of DMF impregnation.The carbon fiber cloth modified by KH550 enhanced its wettability with caprolactam(CPL)melt and was conducive to the all-around encapsulation of PA6 on the surface of the carbon fiber cloth,which effectively solved the problems of uneven dispersion of the carbon fiber cloth in PA6 and poor interfacial bonding.关键词
尼龙6/碳纤维布/表面改性/热塑性复合材料Key words
PA6/carbon fiber cloth/surface modification/thermoplastic composite分类
通用工业技术引用本文复制引用
孔奇胜,唐慧,陈宪宏..尼龙6原位包覆碳纤维布的制备[J].包装学报,2025,17(3):62-68,7.基金项目
湖南省自然科学基金资助项目(2022JJ50004) （2022JJ50004）