中国实用口腔科杂志2025，Vol.18Issue(3)：294-299,6.DOI:10.19538/j.kq.2025.03.007
改良式牙冠延长术和肩领高度对斜折残根抗折性能的影响研究
Effects of modified crown lengthening procedure combined with ferrule height on fracture resistance of oblique fractured residual roots
摘要
Abstract
Objective To study the effects of modified crown lengthening procedure combined with ferrule height on the fracture resistance of mandibular first premolar with oblique fractures restored with fiber post and core crown.Methods Totally forty mandibular first premolars(all single-root canals)extracted at the Department of Oral and Maxillofacial Sur-gery,School and Hospital of Stomatology,Hebei Medical University from April to July 2024 were selected.Following con-ventional root canal treatment,the crowns were severed at a height of 3.0 mm above the lingual enamel-cementum junc-tion and subsequently cut from the lingual section to the buccal at 1.0 mm above the buccal enamel-cementum junction to create the lingual-buccal oblique fractured root mod-els.They were randomly divided into 5 groups(Groups A to E),with 8 in each group.Group A:the control group,designed with a half-wrapped dentin ferrule measuring 2.0 mm on the lingual side and 0 mm on the buccal side;Group B:simulated modified crown lengthening proce-dure,designed with a dentin ferrule measuring 2.0 mm on the lingual side and 1.0 mm on the the buccal side;Groups C,D and E:simulated modified crown lengthening procedure,designed with a full-wrapped dentin ferrule measuring 2.0 mm,3.0 mm and 4.0 mm respectively at the residual root neck.After restoration with preformed glass fiber posts,resin cores and cobalt-chromium metal full crown,the specimens were embedded in self-curing resin blocks.The clinical crown-root ratios(C/R)of the completed Groups A to E were 0.75,0.83,0.91,1.10 and 1.33,respectively.The embedded speci-mens were placed on a universal testing machine and loaded(the loading direction was at an angle of 150°to the long ax-is of the tooth)until fracture.The fracture load values and fracture mode of the specimens were recorded.Results The fracture loads of the specimens in Groups A to E were(1.45±0.10)kN,(1.63±0.07)kN,(1.67±0.09)kN,(0.95±0.12)kN and(0.69±0.18)kN,respectively.There was a statistically significant difference in the fracture loads among the groups(F=112.047,P＜0.001).Further pairwise comparisons between groups revealed that there was no statistical-ly significant difference between Group B and Group C(q=0.494,P=0.957),but there were statistically significant dif-ferences among the other groups(all P＜0.05).Among the fracture mode of each group,only 2 specimens in Groups D and E had fracture surfaces below the cervical one-third of the root,while the fracture surfaces of the other groups were above the cervical one-third,or there were fractures and detachments of the post-core.There was no significant differ-ence in the fracture mode among all groups(x2=6.321,P=0.642).Conclusion In simulating the effects of modified crown lengthening procedure combined with ferrule height on the fracture resistance of mandibular first premolars follow-ing fiber post-core crown restoration,it is found that variations in dentine ferrule height significantly influence the resis-tance of these residual roots after restoration.Specifically,when a fully wrapped dentine ferrule measuring 1.0-2.0 mm is prepared at the residual root neck and the crown-to-root ratio remains below 1,optimal fracture resistance of the teeth can be ensured.关键词
改良式牙冠延长术/牙本质肩领/纤维桩核冠/残根/抗折性能Key words
modified crown lengthening procedure/dentin ferrule/fiber post-core crown/residual roots/fracture resistance分类
医药卫生引用本文复制引用
王晓雪,吴素然,张晓,张立亚..改良式牙冠延长术和肩领高度对斜折残根抗折性能的影响研究[J].中国实用口腔科杂志,2025,18(3):294-299,6.基金项目
河北省卫生健康委员会医学科学研究课题计划项目(20221471) （20221471）