降低中大棒圆钢表面裂纹的攻关与实践
Reducing the Surface Crack of Medium and Large Bar Round Steel and Practice
陈正权1
作者信息
- 1. 福建三钢闽光股份有限公司,福建 三明 365000
- 折叠
摘要
Abstract
In the process of developing and testing round bars,cracks on the surface of finished products frequently occur,and there are quality risks.Through defectmetall ographic analysis,cause analysis,process investigation,taking measures and curing,the generation of surface cracks is reduced,and batch order-taking production is realized.关键词
表面裂纹/金相分析/原因分析/采取措施Key words
surface cracks/metallographic analysis/cause analysis/take action引用本文复制引用
陈正权..降低中大棒圆钢表面裂纹的攻关与实践[J].福建冶金,2025,54(4):35-38,4.