国内丁二烯橡胶(BR)9000性能对比分析
The Comparative Analysis of Properties for the Domestic Butadiene Rubber(BR)9000
黄世英 1陈海华 1刘俊保 1曹帅英 1王震 1王春龙1
作者信息
- 1. 中国石油天然气股份有限公司石油化工研究院 兰州化工研究中心国家合成橡胶质量检验检测中心,甘肃 兰州 730060
- 折叠
摘要
Abstract
Butadiene rubbers(BR)9000 produced by 10 domestic synthetic rubber manufacturers,such as PetroChina,Sinopec and some private enterprises,the molecular weight and distribution,microstructure,properties of raw rubber,properties of vulcanized rubber and vulcanization properties of them were compared according to the national and industrial standards.The results showed that the molecular weight distribution of BR9000 was at the same level and was wider;the volatile component were lower than 0.09％except for enterprises b,d and e;the ash contents were similar;the gel contents were slightly higher of enterprises b and g,and were the same for other firms;the Mooney viscosities of the raw rubber were between 42 and 46,which were basically close;the vulcanization rates were basically the same;the constant elongation stress,tensile strength and elongation at break were all at the same level.The technical indicators for BR9000 of domestic production had reached excellent products of the national standard.关键词
丁二烯橡胶/微观结构/物理机械性能/对比分析Key words
butadiene rubber/microstructure/physical and mechanical properties/comparative analysis分类
化学化工引用本文复制引用
黄世英,陈海华,刘俊保,曹帅英,王震,王春龙..国内丁二烯橡胶(BR)9000性能对比分析[J].合成材料老化与应用,2025,54(5):8-10,3.