超深井耐高温低腐蚀无固相压井液研究
Study on high-temperature resistant,low-corrosion and solid-free well control fluid for ultra-deep wells
摘要
Abstract
Objective This study aims to prepare a high-temperature resistant,low-corrosion,and solid-free well control sluid system suitable for ultra-deep wells,and clarify its temperature resistance,corrosion resistance performances.Method Firstly,two well control fluid systems were prepared using potassium formate and composite salt weighting agents as the basis,supplemented with solubilizers,oxygen scavengers,corrosion inhibitors,etc.Secondly,the low-corrosion resistant performance for these systems was evaluated using electrochemical methods,the high-temperature resistant performance was evaluated using hot rolling test,corrosion weight loss experiment of P110 steel in wellbore working condition was simulated by high temperature and high pressure autoclave,and the corrosion product film's forms and components were analysed by SEM、EDS、XRD methods.Result Both JSY-1 and FHY-1 well control fluid systems with the density up to 1.6 g/cm3 could withstand temperatures up to 180℃.After corrosion in 180℃、2 MPa CO2 pressure dividing wellbore condition,P110 steel corrosion rate in two well control fluid were both below 0.060 mm/a.The corrosion products in potassium formate system JSY-1 were Fe3O4 and FeCO3,and that in composite salt system FHY-1 were Fe3O4、Fe2O3 and CaCO3.Conclusion The developed high-density well conrol fluid has high-temperature resistance、low-corrosion and solid-free characteristics,which can meet the requirement of well control in ultra deep well.关键词
甲酸钾/复合盐/压井液/P110钢/腐蚀性能Key words
potassium formate/compound salt/well control fluid/P110 steel/corrosion performance引用本文复制引用
吴刚,蔡军,史胜垚,杨春华,刘其伦,赵能,王祥稳,曾德智..超深井耐高温低腐蚀无固相压井液研究[J].石油与天然气化工,2025,54(5):65-73,9.基金项目
新型油气勘探开发国家科技重大专项"超深层含硫气井经济高效防腐与排采一体化工艺技术攻关及应用"(2025ZD1402505) （2025ZD1402505）