中国造纸2026，Vol.45Issue(1)：121-133,13.DOI:10.11980/j.issn.0254-508X.2026.01.016
添加肉桂微粉的稠浆法烟草薄片制备工艺优化及性能研究
Optimization of Slurry Process and Performance Study for Reconstituted Tobacco Sheets with Added Cinnamon Micropowder
摘要
Abstract
The orthogonal experiment was employed to optimize the preparation process parameters of slurry processed reconstituted tobacco sheet added with cinnamon micropowder(CRT).A comparative analysis was conducted between the CRT and the control sample(RT)in terms of sensory quality,morphological structure,pyrolysis and combustion characteristics,and mainstream cigarette smoke release profile.The results showed that the optimal process parameters were as follows(based on tobacco powder mass):water addition amount of 550%,broadleaf fiber addition amount of 4.00%,carboxy methylcellulose soclium addition amount of 1.00%,casting thickness of 0.9 mm,and drying temperature of 80℃.The CRT exhibited a pronounced spicy characteristics with enhanced aroma quantity.Its color developed to-wards decreased lightness and increased red tone,presenting a smooth and oily surface.The addition of cinnamon micnpowder had a minor effect on the weight loss process during pyrolysis of the CRT but significantly influenced the combustion process.It reduced the weight loss rate of the coke stage in combustion stage and improved the comprehensive combustion characteristic index.Furthermore,the addition of cinnamon micopowder increased the release of flavor components in the particulate matter of mainstream cigarette smoke from 1 713.58 to 2 003.81 μg/cigarette,introducing the release of characteristic components such as cinnamaldehyde and phenylacetaldehyde.关键词
稠浆法烟草薄片/肉桂微粉/热重分析/工艺优化/烟气释放Key words
slurry processed reconstituted tobacco sheet/cinnamon micropowder/thermogravimetric analysis/process optimization/cigarette smoke分类
轻工纺织引用本文复制引用
吴键,管庆林,卢昕博,赵亮,张嘉辉,梁淼,张峻松,肖卫强..添加肉桂微粉的稠浆法烟草薄片制备工艺优化及性能研究[J].中国造纸,2026,45(1):121-133,13.基金项目
浙江中烟工业有限责任公司科技项目(202333-0000341212) （202333-0000341212）
中国烟草总公司重大科技项目(110202201048(XX-07)). （110202201048(XX-07）