矿渣-粉煤灰地聚物注浆材料配合比优化研究
Mix Ratio Optimization of Slag-Fly Ash Geopolymer Grouting Materials
摘要
Abstract
In order to provide mix ratio design references and theoretical support for the promotion and application of geopolymer grouting materials in road trenchless grouting reinforcement and other projects,for slag-fly ash geopolymer grouting materials(SFGGM),the influences of water-to-binder ratio,alkali equivalent,sodium silicate modulus and fly ash content on multiple key indicators such as fluidity,setting time,drying shrinkage rate and mechanical property were obtained through range analysis and analysis of variance by using four-factor and four-level orthogonal experiments.On this basis,a comprehensive weight analysis of multiple indicators was conducted with AHP-entropy method to select the optimal mix ratio scheme that takes into account workability,volume stability and mechanical property.The results show that the water-to-binder ratio has the most significant impact on fluidity.As the water-to-binder ratio increases,the fluidity of slurry improves significantly.The alkali equivalent is the dominant factor controlling the setting time and drying shrinkage rate.If alkali equivalent is too high,it will lead to shorten setting time and increased drying shrinkage rate.The fly ash content is a key factor affecting compressive strength and flexural strength.Excessive content leads to a decrease in compressive strength and flexural strength.Moderately increasing the alkali equivalent and sodium silicate modulus is conducive to promoting strength development.The main influencing factors of each performance index obtained from range analysis and analysis of variance are consistent.The optimal ratio for comprehensive performance is as follows:water-to-binder ratio 0.6,sodium silicate modulus 1.6,alkali equivalent 6%(mass fraction),and fly ash content 0.4(the proportion of total mass of silicon and aluminum source ash).关键词
地聚物注浆材料/最优配合比/正交试验/AHP-熵值法/极差分析/方差分析Key words
geopolymer grouting material/optimal mix ratio/orthogonal experiment/AHP-entropy method/range analysis/analysis of variance分类
交通工程引用本文复制引用
刘梅芳,刘建正,胡力群,高胜发,刘家宏,李国超..矿渣-粉煤灰地聚物注浆材料配合比优化研究[J].硅酸盐通报,2026,45(2):695-711,17.基金项目
青海省交通科技项目(GM2021咨04) （GM2021咨04）