NiCrAlY is a commonly used metallic bond coat material for thermal barrier coating in gas turbines.This study investigates the effect of two NiCrAlY powders with different aluminum contents for gas turbine fabrication on the thermal cycling behavior of HVOF-NiCrAlY+APS-nanostructured YSZ(nYSZ)thermal barrier coatings(TBCs)within the temperature range from room temperature to 1150℃.The results show that the growth rate of the Al2O3 thermally grown oxide(TGO)on the surface of HVOF-Ni25Cr5Al0.5Y is lower than that of HVOF-Ni22Cr10Al1Y.Similar to the microstructured YSZ(mYSZ)/mYSZ interface,the nYSZ/mYSZ interface can also act as a crack initiation site,leading to the formation of a local crack network in the nYSZ layer.The failure mechanism of two HVOF-NiCrAlY+APS-nYSZ TBCs is consistent with that of the traditional APS/HVOF-MCrAlY(M=Ni and Co)+APS-mYSZ system,which is mainly attributed to the propagation and coalescence of cracks in the nYSZ layer adjacent to the HVOF-NiCrAlY/APS-nYSZ interface.The thermal cycling lifetime of the Ni25Cr5Al0.5Y+APS-nYSZ coating is slightly longer than that of the Ni22Cr10Al1Y+APS-nYSZ coating.Meanwhile,it can effectively improve the thermal cycling life of HVOF-MCrAlY+APS-YSZ TBCs to increase the bonding strength of the YSZ/YSZ interface in the APS-YSZ layer and avoid cracking at the YSZ/YSZ interface and the outer surface of the APS-YSZ.关键词
燃气轮机/热障涂层/HVOF-NiCrAlY/Al含量/APS-nYSZ/热循环行为Key words
gas turbine/thermal barrier coating/HVOF-NiCrAlY/Al content/APS-nYSZ/thermal cycling behavior分类
通用工业技术引用本文复制引用
李超,程玉贤,黎红英,王璐,陈卫杰..Al含量对HVOF-NiCrAlY+APS-nYSZ热障涂层热循环行为的影响[J].航空材料学报,2026,46(3):87-96,10.基金项目
国家青年科学基金(52401093) （52401093）
辽宁省科技重大专项(2024JH1/11700039) （2024JH1/11700039）
辽宁省中央引导地方科技发展资金联合基金(IC24ZXK300) （IC24ZXK300）