塑料科技2026，Vol.54Issue(3)：111-115,5.DOI:10.15925/j.cnki.issn1005-3360.2026.03.020
碳纤维对酚醛树脂复合材料力学性能和耐久性能的影响
Effect of Carbon Fiber on Mechanical Properties and Durability of Phenolic Resin Composites
摘要
Abstract
Carbon fiber(CF)modified by a coupling agent(KH-550)was employed as the reinforcement,and phenolic resin(PF)served as the matrix to fabricate PF/CF composites.The mechanical properties and durability of the composites were subsequently investigated.The results revealed that after CF was modified by KH-550,a new characteristic peak emerged at 990 cm-1 in the Fourier transform infrared spectrum of CF,while the peaks near 1 150 cm-1 and 3 485 cm-1 became broader and significantly intensified,indicating that KH-550 had been successfully grafted onto the CF surface.As the content of modified CF increased,both the tensile strength and flexural strength of the PF/CF composites exhibited a trend of initial increase followed by decrease.The friction resistance first improved and then deteriorated,whereas the heat resistance gradually enhanced.When the mass fraction of modified CF was 6%,the comprehensive mechanical properties and durability of PF/CF composites reached the optimum.Compared with PF,the tensile strength and flexural strength of the composites increased by 119.7%and 55.3%,respectively,the wear rate decreased by 75.6%,the initial thermal decomposition temperature rose by 64℃,and the final mass residual ratio was 2.02 times that of PF.关键词
碳纤维/酚醛树脂/力学性能/耐久性能Key words
Carbon fiber/Phenolic resin/Mechanical properties/Durability performance分类
通用工业技术引用本文复制引用
卫娇,罗冯敏,穆占春,郭丽娜..碳纤维对酚醛树脂复合材料力学性能和耐久性能的影响[J].塑料科技,2026,54(3):111-115,5.基金项目
2025年云南省教育厅科学研究基金项目(2025J1356) （2025J1356）