陕西科技大学学报2026，Vol.44Issue(2)：1-7,7.
国产高透气度医用盖材纸隔离胶的涂胶工艺与胶面性能研究
Study on release coating process and coated surface properties of domestic high-breathability medical cover paper
摘要
Abstract
To achieve domestic substitution of medical high-breathability cover paper sub-strates and develop high-strength,high-permeability medical packaging materials,this study comparatively analyzed the coatability of domestic and imported base papers.A single-layer release coating process with pore-forming agent hybrid primer was adopted,investigating air permeability,surface properties,wettability,and interlayer adhesion evolution between the base paper and composite release layer under varying formulation ratios.Results indicate that at 3.0 g·m-2 coating weight with 3％pore-former ratio,the composite release-coated paper exhibits excellent coatability:air permeability 733 mL·min-1,uniformity index 88.43,smoothness 3.85 s,roughness 8.14 μm,Cobb60 21.3 g·m-2,contact angle 123 °,interlayer adhesion(MD/CD:0.156 N.m/0.148 N.m).After applying 6.0 g·m-2 hot-melt adhesive,permeability remains at 275 mL·min-1,and heat-sealing with PET achieves peel strength of 5.13～5.90 N·15 mm-1 with clean delamination.This study overcomes the air permeability control limitations of imported base paper,providing key technological support for industrial-scale production of high-performance domestic medical cover paper.关键词
医用盖材纸/高透气度/表面涂胶适应性/附着强度/热封剥离力Key words
medical cover paper/high breathability/surface coatability/adhesion strength/heat-seal peel strength分类
轻工纺织引用本文复制引用
杨园园,徐永建,谢吉利,赵伟..国产高透气度医用盖材纸隔离胶的涂胶工艺与胶面性能研究[J].陕西科技大学学报,2026,44(2):1-7,7.基金项目
国家自然科学基金项目(22171172) （22171172）
企业横向研究项目(210230252) （210230252）